|Material:||Alumina Ceramics||Name:||Ceramic Crucible|
|Color:||White,red||Features:||High Voltage Withstand And Excellent Mechanical Properties|
|Voltage:||15000v Withstand||Forming Method:||Injection Molding|
|Shape:||Saggar||Product Name:||Alumina Ceramic Al2o3 Fire Clay Crucible|
Alumina Crucible 15000v,
15000v Al2o3 Crucible,
15000v alumina saggar
The capacity of the alumina crucible is 5 to 2000ml according to appearance, maximum capacity can be customized, and maximum size is 450mm. Under the general condition, the analyzed and fired substance is put into the alumina crucible or a sagger and then put into analyzing or firing equipment to be heated. Heating and cooling speed is different according to the characteristics of the equipment and products. A raw material for manufacturing the alumina crucible and the sagger is subjected to thermal expansion, and the alumina crucible and the sagger are easily cracked if the heating or cooling speed is overhigh, so that the speed had better be low to prolong the service life of the crucible and the sagger. A corundum crucible contains 99.70% of corundum, has good high temperature insulation property and mechanical strength at the temperature of 1650 to 1700℃ in oxidizing atmosphere and reducing atmosphere, high heat conductivity and low thermal expansivity, does not react with air, water vapor, hydrogen, carbon monoxide and so on at the temperature of more than 1700℃, and has the short-term maximum service temperature of 1800℃.
Alumina consists of oxidized aluminium and is the most popular among all fine ceramics.
High-purity alumina ceramic series is the ceramic material with Al2O3 content 99.5% and 99.9%.
A. Electrical Insulating properties
B. Wear Resistance
C. Heat Resistance
D. Corrosion Resistance
E. Plasma Resistance
|Material code||characteristics||Density(g/cm³)||Young's Moulus(GPa)||Flexural strength(MPa)||Fracture Toughness(MPa*m1/2)||Thermal Expansion RT~800°)||Thermal Conductivity(w/m*k)||Volume Resistivity(Ω*cm)|
|ALP01||General Purpose High Rigidiy||3.9||370||440||3~4||7.7||33||＞10⋀14|
|ALP02||High Purity High Rigidity||3.9||370||450||3~4||7.9||30||＞10⋀14|
Wuxi Special Ceramic Electrical mainly produces alumina, Silicon nitride, Zirconia, Steatite, Boron nitride, Cordierite,mullite products, widely used in metal welding, electronic conductor, mechanics, assembling, insulation, chemicals, instrument, textile, nuclear industry, aerial field.We accept trial produce according to the drawing or sample.It usually takes 15 days to finish trial product.Mass produce usually takes 30 days.Goods' package is carton or PLT.It can be negotiable with each other.
We mainly sell goods to toshiba lighting group in Japan and Europe.Our aim is to deliver goods with high quality at quick delivery date.
quality guarantee:mass produce by 100% inspection